Alumina Seal Ceramic Rings / Industry Insulation Rings
1. Description:
Alumina ceramic heating element vs PTC ceramic heating element
Electric heaters heating constant heat field pipes: Under the same
conditions, when a fixed voltage is applied, the air heating effect
of MCH electric heaters is better than that of PTC electric
heaters.Closed space heating test: In terms of power consumption,
MCH saves energy by 24.59% compared to PTC.
Heating silicone oil comparison test: Use silicone oil as the
heating and conduction medium to compare the heating performance
and power consumption of PTC and MCH heating components. , Under
the same conditions as other conditions, the heating effect of MCH
heating element heating silicone oil is significantly better than
that of PTC heating element under the premise of consuming the same
power.
2. Feature Advantages:
1) Refractory, High Temperature Resistance, Maximum Used
Temperature: 1800 ºC (3272ºF)
2) Hardness Strength, Wear Resistance Up To Mohz 9.0 ; HRA 80-90
3) High Voltage, Good Insulation Performance ,Electrical
Resistivity Up To 10∧14 Ohm.Cm
4) High Polished Surface Up To Rz0.8(Ra0.1)
5) Superior Mechanical Strength, MAX 10 MPa.m1/2 Fracture toughness
6) Pressure Resistance, Max 2300MPa compressive strength
7) Anti-High Corrosion Resistance, Such As Acid Alkali Resistance
8) Long Service Life
9) Other excellent property
3. Material Features / Properties:
| Composite | (wt %) | 99% | 99.5% | 99.8% |
| Color | | White or Ivory | White or Ivory | White or Ivory |
| Density | g/cm 3 | 3.82 | 3.9 | 3.92 |
| Hardness | HRA | 83 | 85 | 85 |
| Flexural Strength | Mpa (psi*10 3 ) | 375 | 386 | 381 |
4. Technical Parameters:
| Technical Parameters of Ceramics |
| Items | Test Conditions | Unit or Symbol | 99% AL2O3 | 95% AL2O3 | 90% AL2O3 | Zirconia | Steatite | Silicon Carbide |
| Volume Density | -- | g/cm3 | ≥3.70 | ≥3.62 | ≥3.40 | ≥5.90 | ≥2.60 | ≥3.08 |
| Tightness | -- | Pa·m³/s | ≤1.0×10-11 | ≤1.0×10-11 | ≤1.0×10-11 | - | - | - |
| Liquid Permeability | -- | -- | Pass | Pass | Pass | | Pass | - |
| Flexural Strength | - | MPa | ≥300 | ≥280 | ≥230 | ≥1100 | ≥120 | ≥400 |
| Elastic Modulus | - | GPa | - | ≥280 | ≥250 | ≥220 | - | 400 |
| Poisson Ratio | - | - | - | 0.20～0.25 | 0.20～0.25 | - | - | - |
| Thermal Shock Resistance | 800℃( Room Temperature) Cycle: 10 times | | Pass | Pass | Pass | - | - | - |
| Coefficient of Linear Expansion | 20℃～100℃ | ×10-6 K-1 | - | - | - | | ≤8 | - |
| 20℃～500℃ | ×10-6 K-1 | 6.5～7.5 | 6.5～7.5 | 6.5～7.5 | 6.5～11.2 | - | - |
| 20℃～800℃ | ×10-6 K-1 | 6.5～8.0 | 6.5～8.0 | 6.3～7.3 | | - | 4 |
| 20℃～1200℃ | ×10-6 K-1 | - | 7.0～8.5 | - | - | - | - |
| Coefficient of Thermal Conductivity | 20℃ | W/(m·k) | - | - | - | - | - | 90～110 |
| 1000℃ |
| Dielectric Constant | 1MHz 20℃ | - | 9.0～10.5 | 9.0～10 | 9.0～10 | - | ≤7.5 | - |
| 1MHz 50℃ | - | - | 9.0～10 | - | - | - | - |
| 10GHz 20℃ | - | 9.0～10.5 | 9.0～10 | 9.0～10 | - | - | - |
| Volume Resistivity | 100℃ | Ω·cm | ≥1.0×1013 | ≥1.0×1013 | ≥1.0×1013 | - | ≥1.0×1012 | - |
| 300℃ | ≥1.0×1013 | ≥1.0×1010 | ≥1.0×1013 | - | - | - |
| 500℃ | ≥1.0×109 | ≥1.0×108 | -- | - | - | - |
| Disruptive Strength | D.C | kV/mm | ≥17 | ≥15 | ≥15 | - | ≥20 | - |
| Chemical Durability | 1:9HCl | mg/c㎡ | ≤0.7 | ≤7.0 | - | - | - | - |
| 10%NaOH | mg/c㎡ | ≤0.1 | ≤0.2 | - | -- | - | - |
| Grain Size | - | μm | - | 3~12 | - | - | - | - |
5. Process Flows:
Formulating --- Granulating --- Forming --- Sintering --- Grinding
--- Printing --- Nickel Plating --- Assembing --- Brazing ---
Inspecting --- Packing
6. Production Facilities: Prilling Tower , Forming Machine , High
Temperature Sintering Kiln
7. Detection Devices:
Electric Performance Tester , Film Thickness Analyzer ,
Granulometer , Helium Mass Spectrometer Leak Detector , Universal
Pull Force Meter
8. Our advantages: Quality Assurance ; Price Competitive ; Factory Supply Directly ;
Good Service
9. Shipping and Package:
10. Our aimed market:
Notes:Above information only for reference and please contact with
us for more details freely when you have any inquiry!