Home Electrical Microwave Magnetron Ceramic / Special Ceramic Parts
1. Description:
A great variety of ceramics have been successfully sintered using
microwaves over the past 30 years:
structural ceramics (Al203,
ZnO, SiC, MgAl2O4, Y–PSZ, Y–TZP/Al2O3, TiO2),
bioceramics (hydroxyapatite),
functional ceramics (ZnO,BaTiO3), composites (MgO–Y2O3, ZrB2–B4C, WC–Co), magnetic ceramics (Ni–Zn ferrites), translucent or transparent ceramics (AlN, MgO,
ALON)… Details can be found in various review papers (Das et al., 2009; Karayannis, 2016; Katz, 1992; Oghbaei and Mirzaee, 2010). Experiments involve a high diversity of frequencies (from 915
MHz to 50 GHz and above), of cavities (single mode, multimode,
rectangular or cylindrical), using direct, hybrid or indirect
heating.
2. Feature Advantages:
1) High elasticity modulus
2) High compressive strength.
3) Anti corrosion
4) Abrasion resistance
5) Impact resistance
6) High precision
7) High stability
8) Good advanced ceramic materials
9) High welding sealing performance
10) High hardness and high density
11) Low thermal conductivity
12) Chemical inertness
13) Good wear resistance
14) High Fracture toughness
15) Good insulation performance
16) High temperature resistance
3. Material Features / Properties:
| Composite | (wt %) | 99% | 99.5% | 99.8% |
| Color | | White or Ivory | White or Ivory | White or Ivory |
| Density | g/cm 3 | 3.82 | 3.9 | 3.92 |
| Hardness | HRA | 83 | 85 | 85 |
| Flexural Strength | Mpa (psi*10 3 ) | 375 | 386 | 381 |
4. Technical Parameters:
| Technical Parameters of Ceramics |
| Items | Test Conditions | Unit or Symbol | 99% AL2O3 | 95% AL2O3 | 90% AL2O3 | Zirconia | Steatite | Silicon Carbide |
| Volume Density | -- | g/cm3 | ≥3.70 | ≥3.62 | ≥3.40 | ≥5.90 | ≥2.60 | ≥3.08 |
| Tightness | -- | Pa·m³/s | ≤1.0×10-11 | ≤1.0×10-11 | ≤1.0×10-11 | - | - | - |
| Liquid Permeability | -- | -- | Pass | Pass | Pass | | Pass | - |
| Flexural Strength | - | MPa | ≥300 | ≥280 | ≥230 | ≥1100 | ≥120 | ≥400 |
| Elastic Modulus | - | GPa | - | ≥280 | ≥250 | ≥220 | - | 400 |
| Poisson Ratio | - | - | - | 0.20～0.25 | 0.20～0.25 | - | - | - |
| Thermal Shock Resistance | 800℃( Room Temperature) Cycle: 10 times | | Pass | Pass | Pass | - | - | - |
| Coefficient of Linear Expansion | 20℃～100℃ | ×10-6 K-1 | - | - | - | | ≤8 | - |
| 20℃～500℃ | ×10-6 K-1 | 6.5～7.5 | 6.5～7.5 | 6.5～7.5 | 6.5～11.2 | - | - |
| 20℃～800℃ | ×10-6 K-1 | 6.5～8.0 | 6.5～8.0 | 6.3～7.3 | | - | 4 |
| 20℃～1200℃ | ×10-6 K-1 | - | 7.0～8.5 | - | - | - | - |
| Coefficient of Thermal Conductivity | 20℃ | W/(m·k) | - | - | - | - | - | 90～110 |
| 1000℃ |
| Dielectric Constant | 1MHz 20℃ | - | 9.0～10.5 | 9.0～10 | 9.0～10 | - | ≤7.5 | - |
| 1MHz 50℃ | - | - | 9.0～10 | - | - | - | - |
| 10GHz 20℃ | - | 9.0～10.5 | 9.0～10 | 9.0～10 | - | - | - |
| Volume Resistivity | 100℃ | Ω·cm | ≥1.0×1013 | ≥1.0×1013 | ≥1.0×1013 | - | ≥1.0×1012 | - |
| 300℃ | ≥1.0×1013 | ≥1.0×1010 | ≥1.0×1013 | - | - | - |
| 500℃ | ≥1.0×109 | ≥1.0×108 | -- | - | - | - |
| Disruptive Strength | D.C | kV/mm | ≥17 | ≥15 | ≥15 | - | ≥20 | - |
| Chemical Durability | 1:9HCl | mg/c㎡ | ≤0.7 | ≤7.0 | - | - | - | - |
| 10%NaOH | mg/c㎡ | ≤0.1 | ≤0.2 | - | -- | - | - |
| Grain Size | - | μm | - | 3~12 | - | - | - | - |
5. Process Flows:
Formulating --- Granulating --- Forming --- Sintering --- Grinding
--- Printing --- Nickel Plating --- Inspecting --- Packing
6. Application Fields:
Microwave Magnetron Ceramic for Home Electrical Appliances ,
Aerospace and Other Industry!
7. Production Facilities: Prilling Tower , Forming Machine , High
Temperature Sintering Kiln
8. Detection Devices:
Electric Performance Tester , Film Thickness Analyzer ,
Granulometer , Helium Mass Spectrometer Leak Detector , Universal
Pull Force Meter
9. Notes:Above information only for reference and please contact
with us for more details freely when you have any inquiry!