1. Description:
While Y-PSZ is excellent for demanding mechanical applications, it
may not be suitable for very high temperature applications because
it suffers from grain boundary sliding; this occurs when prolonged
exposure to heat causes the material to transform form the strong
tetragonal phase to the weaker monoclinic phase. Similarly, it may
not be suitable for warm and moist conditions since its properties
deteriorate when it is exposed to water vapor. YSZ is therefore
best suited when it is operating in dry and moderate temperature
conditions. For more information on hydrothermal aging of Zirconia
please contact us.
2. Feature Advantages:
1) High density.
2) High fracture toughness .
3) High hardness High Mechanical Strength.
4) Low thermal conductivity Excellent insulation .
5) Good Wear resistance.
6) Resistant to Corrosion and Chemical Attack.
7) Extreme Temperature Stability.
8) Outstanding Electrical and Electronic Properties.
3. Material Features / Properties:
| Composite | (wt %) | 99% | 99.5% | 99.8% |
| Color | | White or Ivory | White or Ivory | White or Ivory |
| Density | g/cm 3 | 3.82 | 3.9 | 3.92 |
| Hardness | HRA | 83 | 85 | 85 |
| Flexural Strength | Mpa (psi*10 3 ) | 375 | 386 | 381 |
4. Technical Parameters:
| Technical Parameters of Ceramics |
| Items | Test Conditions | Unit or Symbol | 99% AL2O3 | 95% AL2O3 | 90% AL2O3 | Zirconia | Steatite | Silicon Carbide |
| Volume Density | -- | g/cm3 | ≥3.70 | ≥3.62 | ≥3.40 | ≥5.90 | ≥2.60 | ≥3.08 |
| Tightness | -- | Pa·m³/s | ≤1.0×10-11 | ≤1.0×10-11 | ≤1.0×10-11 | - | - | - |
| Liquid Permeability | -- | -- | Pass | Pass | Pass | | Pass | - |
| Flexural Strength | - | MPa | ≥300 | ≥280 | ≥230 | ≥1100 | ≥120 | ≥400 |
| Elastic Modulus | - | GPa | - | ≥280 | ≥250 | ≥220 | - | 400 |
| Poisson Ratio | - | - | - | 0.20～0.25 | 0.20～0.25 | - | - | - |
| Thermal Shock Resistance | 800℃( Room Temperature) Cycle: 10 times | | Pass | Pass | Pass | - | - | - |
| Coefficient of Linear Expansion | 20℃～100℃ | ×10-6 K-1 | - | - | - | | ≤8 | - |
| 20℃～500℃ | ×10-6 K-1 | 6.5～7.5 | 6.5～7.5 | 6.5～7.5 | 6.5～11.2 | - | - |
| 20℃～800℃ | ×10-6 K-1 | 6.5～8.0 | 6.5～8.0 | 6.3～7.3 | | - | 4 |
| 20℃～1200℃ | ×10-6 K-1 | - | 7.0～8.5 | - | - | - | - |
| Coefficient of Thermal Conductivity | 20℃ | W/(m·k) | - | - | - | - | - | 90～110 |
| 1000℃ |
| Dielectric Constant | 1MHz 20℃ | - | 9.0～10.5 | 9.0～10 | 9.0～10 | - | ≤7.5 | - |
| 1MHz 50℃ | - | - | 9.0～10 | - | - | - | - |
| 10GHz 20℃ | - | 9.0～10.5 | 9.0～10 | 9.0～10 | - | - | - |
| Volume Resistivity | 100℃ | Ω·cm | ≥1.0×1013 | ≥1.0×1013 | ≥1.0×1013 | - | ≥1.0×1012 | - |
| 300℃ | ≥1.0×1013 | ≥1.0×1010 | ≥1.0×1013 | - | - | - |
| 500℃ | ≥1.0×109 | ≥1.0×108 | -- | - | - | - |
| Disruptive Strength | D.C | kV/mm | ≥17 | ≥15 | ≥15 | - | ≥20 | - |
| Chemical Durability | 1:9HCl | mg/c㎡ | ≤0.7 | ≤7.0 | - | - | - | - |
| 10%NaOH | mg/c㎡ | ≤0.1 | ≤0.2 | - | -- | - | - |
| Grain Size | - | μm | - | 3~12 | - | - | - | - |
5. Process Flows:
Formulating --- Granulating --- Forming --- Sintering --- Grinding
--- Printing --- Nickel Plating --- Assembing --- Brazing ---
Inspecting --- Packing
6. Application Fields:
Widely apply for new energy vehicles, charging piles, solar power
generation, energy storage and power storage system, electric
vehicle power system and so on.
7. Production Facilities: Prilling Tower , Forming Machine , High
Temperature Sintering Kiln
8. Detection Devices:
Electric Performance Tester , Film Thickness Analyzer ,
Granulometer , Helium Mass Spectrometer Leak Detector , Universal
Pull Force Meter
9.Order Flow Steps as belows: Inquiry ---Quotation --- Place an
order --- Production --- Delivery
10. Our advantages: Quality Assurance ; Price Competitive ; Factory Supply Directly ;
Good Service
11.Shipping and Package:
12. Our aimed market :
Notes:Above information only for reference and please contact with
us for more details freely when you have any inquiry!