Zirconia Drawing Machine Tower Round , Wire Wheels , Reel.
1. Description:
The transformation of Zirconia from tetragonal to monoclinic is
large around 5%. It results in limiting its elasticity and fracture
and formation of cracks in zirconia ceramics. Zirconia is mixed
with calcium oxide (CaO),
magnesia (MgO), or yttria (Y2O3) to stabilize in tetragonal or cubic phase.
Partially Stabilized Zirconia (PSZ) consists of cubic, tetragonal,
including monoclinic phases of zirconia. Tetragonal zirconia
polycrystals (TZP) are the purest form of the tetragonal phase compared with
other phases. PSZ and TZP are considered for fabrication of the
biomedical device and scaffolds. Tables 1.7 and 1.8 summarize the mechanical properties of zirconia ceramics. The
strength and fracture toughness of Yttria-TZP ceramics is quite
considerable and almost twice that of alumina. Therefore, zirconia
heads are less susceptible to the stress when contacting with metal
cones. Nowadays most medical-grade zirconia from PSZ tetragonal
zirconia is considered for medical device development. It shows
minimal
microhardness and elastic modulus, good strength, and fracture toughness than
that of alumina. Developing ceramic ball heads below 32 mm is possible from Zirconia as it has superior mechanical
strength.
2. Feature Advantages:
1) High density.
2) High fracture toughness .
3) High hardness High Mechanical Strength.
4) Low thermal conductivity Excellent insulation .
5) Good Wear resistance.
6) Resistant to Corrosion and Chemical Attack.
7) Extreme Temperature Stability.
8) Outstanding Electrical and Electronic Properties.
3. Material Features / Properties:
| Composite | (wt %) | 99% | 99.5% | 99.8% |
| Color | | White or Ivory | White or Ivory | White or Ivory |
| Density | g/cm 3 | 3.82 | 3.9 | 3.92 |
| Hardness | HRA | 83 | 85 | 85 |
| Flexural Strength | Mpa (psi*10 3 ) | 375 | 386 | 381 |
4. Technical Parameters:
| Technical Parameters of Ceramics |
| Items | Test Conditions | Unit or Symbol | 99% AL2O3 | 95% AL2O3 | 90% AL2O3 | Zirconia | Steatite | Silicon Carbide |
| Volume Density | -- | g/cm3 | ≥3.70 | ≥3.62 | ≥3.40 | ≥5.90 | ≥2.60 | ≥3.08 |
| Tightness | -- | Pa·m³/s | ≤1.0×10-11 | ≤1.0×10-11 | ≤1.0×10-11 | - | - | - |
| Liquid Permeability | -- | -- | Pass | Pass | Pass | | Pass | - |
| Flexural Strength | - | MPa | ≥300 | ≥280 | ≥230 | ≥1100 | ≥120 | ≥400 |
| Elastic Modulus | - | GPa | - | ≥280 | ≥250 | ≥220 | - | 400 |
| Poisson Ratio | - | - | - | 0.20～0.25 | 0.20～0.25 | - | - | - |
| Thermal Shock Resistance | 800℃( Room Temperature) Cycle: 10 times | | Pass | Pass | Pass | - | - | - |
| Coefficient of Linear Expansion | 20℃～100℃ | ×10-6 K-1 | - | - | - | | ≤8 | - |
| 20℃～500℃ | ×10-6 K-1 | 6.5～7.5 | 6.5～7.5 | 6.5～7.5 | 6.5～11.2 | - | - |
| 20℃～800℃ | ×10-6 K-1 | 6.5～8.0 | 6.5～8.0 | 6.3～7.3 | | - | 4 |
| 20℃～1200℃ | ×10-6 K-1 | - | 7.0～8.5 | - | - | - | - |
| Coefficient of Thermal Conductivity | 20℃ | W/(m·k) | - | - | - | - | - | 90～110 |
| 1000℃ |
| Dielectric Constant | 1MHz 20℃ | - | 9.0～10.5 | 9.0～10 | 9.0～10 | - | ≤7.5 | - |
| 1MHz 50℃ | - | - | 9.0～10 | - | - | - | - |
| 10GHz 20℃ | - | 9.0～10.5 | 9.0～10 | 9.0～10 | - | - | - |
| Volume Resistivity | 100℃ | Ω·cm | ≥1.0×1013 | ≥1.0×1013 | ≥1.0×1013 | - | ≥1.0×1012 | - |
| 300℃ | ≥1.0×1013 | ≥1.0×1010 | ≥1.0×1013 | - | - | - |
| 500℃ | ≥1.0×109 | ≥1.0×108 | -- | - | - | - |
| Disruptive Strength | D.C | kV/mm | ≥17 | ≥15 | ≥15 | - | ≥20 | - |
| Chemical Durability | 1:9HCl | mg/c㎡ | ≤0.7 | ≤7.0 | - | - | - | - |
| 10%NaOH | mg/c㎡ | ≤0.1 | ≤0.2 | - | -- | - | - |
| Grain Size | - | μm | - | 3~12 | - | - | - | - |
5. Process Flows:
Formulating --- Granulating --- Forming --- Sintering --- Grinding
--- Printing --- Nickel Plating --- Assembing --- Brazing ---
Inspecting --- Packing
6. Application Fields:
Widely apply for new energy vehicles, charging piles, solar power
generation, energy storage and power storage system, electric
vehicle power system and so on.
7. Production Facilities: Prilling Tower , Forming Machine , High
Temperature Sintering Kiln
8. Detection Devices:
Electric Performance Tester , Film Thickness Analyzer ,
Granulometer , Helium Mass Spectrometer Leak Detector , Universal
Pull Force Meter
9. Order Flow Steps as belows: Inquiry ---Quotation --- Place an
order --- Production --- Delivery
10. Our advantages: Quality Assurance ; Price Competitive ; Factory Supply Directly ;
Good Service
11.Shipping and Package:
12. Our aimed market :
Notes:Above information only for reference and please contact with
us for more details freely when you have any inquiry!